Ocean Blue
FINISHES APPARENT DENSITY 2630 KG/M3 WATER ABSORPTION (%) 3.60% OPEN POROSITY (%) 1.70% FLEXURAL STRENGTH 14.9MPA COMPRESSION RESISTANCE 51.9MPA ABRASION […]
Beige CM Fine Grain
FINISHES APPARENTLY DENSITY 2450 KG/M3 WATER ABSORPTION (%) 3.10% OPEN POROSITY (%) 7.70% MECHANICAL RESISTANCE TO BENDING 11.4MPA MECHANICAL RESISTANCE […]
Moca Medium grain cross-cut
APPARENTLY DENSITY 2436 KG/M3 WATER ABSORPTION (%) 1.8% OPEN POROSITY (%) 4.4% MECHANICAL RESISTANCE TO BENDING 6.3 MPA MECHANICAL RESISTANCE […]
Moca Cream Classic
FINISHES APPARENT DENSITY 2363 KG/M3 WATER ABSORPTION (%) 1.80% OPEN POROSITY (%) 4.40% FLEXURAL STRENGTH 6.3MPA COMPRESSION RESISTANCE 55MPA ABRASION […]
Cream Casais
FINISHES APPARENT DENSITY 2363 KG/M3 WATER ABSORPTION (%) 3.60% OPEN POROSITY (%) 10% FLEXURAL STRENGTH 12.5MPA COMPRESSION RESISTANCE 62.3MPA ABRASION […]
Relvinha cross-cut
FINISHES APPARENT DENSITY 2327 KG/M3 WATER ABSORPTION (%) 1.51% OPEN POROSITY (%) 3.5% FLEXURAL STRENGTH 9.12MPA COMPRESSION RESISTANCE 25.98MPA ABRASION […]
Rosal Grey
APPARENT DENSITY 2436 KG/M3 WATER ABSORPTION (%) 1.80% OPEN POROSITY (%) 4.40% FLEXURAL STRENGTH 6.3MPA COMPRESSION RESISTANCE 55MPA ABRASION RESITANCE […]
Moca Blue lake
APPARENT DENSITY 2436 KG/M3 WATER ABSORPTION (%) 1.80% OPEN POROSITY (%) 4.40% FLEXURAL STRENGTH 6.3MPA COMPRESSION RESISTANCE 55MPA ABRASION RESITANCE […]
Ocean Blue
FINISHES APPARENT DENSITY 2630 KG/M3 WATER ABSORPTION (%) 3.60% OPEN POROSITY (%) 1.70% FLEXURAL STRENGTH 14.9MPA COMPRESSION RESISTANCE 51.9MPA ABRASION […]
Beige CM Fine Grain
FINISHES APPARENTLY DENSITY 2450 KG/M3 WATER ABSORPTION (%) 3.10% OPEN POROSITY (%) 7.70% MECHANICAL RESISTANCE TO BENDING 11.4MPA MECHANICAL RESISTANCE […]
Moca Medium grain cross-cut
APPARENTLY DENSITY 2436 KG/M3 WATER ABSORPTION (%) 1.8% OPEN POROSITY (%) 4.4% MECHANICAL RESISTANCE TO BENDING 6.3 MPA MECHANICAL RESISTANCE […]
Ocean Blue
FINISHES APPARENT DENSITY 2630 KG/M3 WATER ABSORPTION (%) 3.60% OPEN POROSITY (%) 1.70% FLEXURAL STRENGTH 14.9MPA COMPRESSION RESISTANCE 51.9MPA ABRASION […]
Beige CM Fine Grain
FINISHES APPARENTLY DENSITY 2450 KG/M3 WATER ABSORPTION (%) 3.10% OPEN POROSITY (%) 7.70% MECHANICAL RESISTANCE TO BENDING 11.4MPA MECHANICAL RESISTANCE […]